Product Description


This product is based on high weather-resistant acrylic emulsion and hydrophilic isocyanate as the main film-forming material.

Incorporate additives that absorb infrared and ultraviolet radiation to achieve a reduction in ground temperature and mitigate the urban heat island effect.

After coating, this product can effectively reduce the temperature range of colored road surfaces by 4-6 degrees Celsius under the same sunlight and environmental temperature, enhancing walking comfort.

Water-soluble high molecular polymer, effectively covering road cracks and depressions, reflecting ultraviolet rays, reducing rain erosion, delaying asphalt aging, and lowering the urban heat conduction effect, decreasing road surface temperature by 2-4 degrees Celsius.


Sample Image

Advantages

1. Easy to install;

2. Excellent durability and color stability.

3. Environmental Protection

4. Chemical-resistant

5. Excellent anti-slip performance.


Application Scenario

1. Park and amusement facilities

2. Pedestrian walkways

3. Bankscapes, parking lots, plazas.

4. Bike lanes and road surfaces.


Technical Standard Requirements

Comply with the technical specifications and requirements for colored road surface as stipulated in the "Technical Code for Color Asphalt Concrete Road Surface in Urban Roads."

2. Complies with the relevant provisions of the national traffic industry standard JT/T712-2008 "Road Anti-Slip Coating" for cold-applied anti-slip coatings.

Film appearance: After drying and shaping, the color and aggregate particle distribution should be even, without cracks or aggregate particle shedding.

(2) Water resistance: No abnormal phenomena should occur after soaking in water for 24 hours.

(3) Alkaline Resistance: No abnormal phenomena observed after soaking in a saturated calcium hydroxide solution for 24 hours.

(4) Low-temperature crack resistance of coating: Maintain at -10℃ for 4 hours, then place at room temperature for 4 hours as one cycle. After three consecutive cycles, there should be no cracks.

(5) Skid Resistance: BPN ≥ 70

3. Environmental Protection Technical Requirements: SP colored road paint must not contain benzene, toluene, ethylbenzene, and xylene. The Volatile Organic Compounds (VOC) content must be less than 15g/L, and the free formaldehyde content must be less than 15mg/L. The heavy metal content requirements are: lead < 10mg/kg, chromium < 5mg/kg, mercury < 2mg/kg, and cadmium < 5mg/kg.



Physical Properties


Serial Number

Inspection Items

Technical specification requirements

Note

1

Applicable Traffic Grade

Light traffic


2

Film appearance

After drying and molding, the color and distribution of aggregate particles should be uniform, without cracks or any aggregate particles falling off.


3

Water resistance

Soak in water for 24 hours should show no abnormal phenomena.


4

Alkali resistance

The calcium hydroxide saturated solution was soaked for 24 hours without any abnormal phenomena.


5

Low-temperature crack resistance of coating

Maintain -10℃ for 4 hours, then leave at room temperature for 4 hours, forming one cycle. After three consecutive cycles, no cracks should be present.


6

The base material's condition within the container

Should be free of lumps and skin, easy to blend.


7

VOC Testing

≤15g/L


8

Setting Time

≥10min


9

Base Material Adhesion (Circle Method)

≤ 4th grade


10

Non-stick mold drying time (quick-dry cold coating type)

≤60min


11

Spray Thickness

≥10min


12

Anti-slip properties

High anti-slip (BPN ≥ 70)


13

Heavy metal content (refer to the requirements for heavy metals in the "Standard for Floor Coating Materials" GBT 22374-2008: Water-based materials: Lead ≤30mg/kg, Cadmium ≤30mg/kg, Hexavalent Chromium ≤30mg/kg, Mercury ≤10mg/kg)

Barium (Ba) < 5ppm

Sb (Antimony) < 5ppm


Cr (Chromium) < 8ppm

Pb (Lead) < 10 ppm


Ag (Silver) < 5ppm

As < 5ppm


Hg (Mercury) < 5ppm

Cd (cadmium) < 7ppm


Se (Selenium) < 1ppm



 

Material processing

Pavement foundation requirements

1. The concrete pavement requires a strength of C25 or higher, and construction can only commence after the pavement has fully cured and dried.

2. Recommended asphalt concrete mix ratio for asphalt concrete pavement is AC-10 or AC-13 fine-grained dense gradation asphalt concrete.



Structure Diagram

Construction


1. Clear the road surface and apply masking tape or protective film along the edges.

2. Mechanical spraying or manual brushing of facial cleansers;

3. Apply or scrape a flexible primer coating.

4. After the base coat cures for 4 hours at 25°C, apply the anti-slip abrasion-resistant layer.

5. Spray or roll-on surface protective agents.



Usage


Base material: Concrete, tiles, marble, steel plate

Base Coat: 0.2 kg/sq. meter

2. Flexible Base Adhesive Structure Layer: 1.6 kg/sq. meter

3. Anti-slip Abrasion Layer: 0.8 kg/sq. meter


Base material is asphalt pavement

Flexible bottom adhesive layer: 2 kg/square meter

2. Anti-slip Abrasion Layer: 0.8 kg/sq. meter


Packaging Specifications

  

Base coat: 15kg per drum, structural layer, wear layer: 25kg per drum


Storage


All components should be stored in a cool, dry environment, out of direct sunlight, in compliance with on-site safety and regulations. Storage temperature should not exceed 35°C, and keep away from open flames and food.


Under proper storage conditions, stored in a sealed drum, shelf life is 12 months. If the product is stored beyond the 12-month shelf life, please contact the relevant departments at Maike Lu before use.


Safety


Please refer to the product manual before use or follow the guidance of the sales engineer.