Alcohol-Resistant Silver Plating Epoxy Resin 2618

Product Introduction:

Features:

Advantages: Solve the problem of powder loss in electroplated silver powder paint, allowing electroplated silver powder paint to be

1. Excellent adhesion for aluminum silver powder and electroplated silver paste; no need for LTW anti-silver shedding additive. Good storage without powder shedding after 100 squares.

2. Significantly improves the brightness of silver powder, enhancing the metallic texture of aluminum silver paste; closely mimics the effect of chrome plating, with strong metallic feel.

2618 (Made in Taiwan) Alcohol-Resistant Silver Plated Resin

Composition: (No LTW/APW anti-sagging agent needed; silver powder doesn't turn black or revert; coated with PU glossy varnish for 100 squares without paint chipping)

Acrylic-modified polymer

Property: Eliminates the hassle of adding anti-blackening silver additives to the degreaser, silver oil doesn't turn black, reducing costs and saving trouble, enhancing competitiveness!

Appearance: Transparent light blue liquid

Glass Transition Temperature: 108℃

Density: 0.925-0.960

Solvent: Special Mixed Active Solvent

Features:

Advantages: Solve the problem of silver powder paint chipping off, allowing the silver powder paint to last longer

1. Exceptional adhesion for aluminum silver powder and electroplate-like silver paste; no need for LTW anti-silver shedding additive; good powder retention and storage after 100-point test.

2. Significantly enhances the brightness of silver powder, boosting the metallic texture of aluminum silver paste; achieves a chrome-like effect with strong metallic feel.

3. Arrange to enhance the opacity of metal pigments; this can reduce the usage of aluminum silver paste and create an extremely fine electroplated metal-like finish.

4. Simple operation and high solid content allow for the addition of more diluent (water), reducing production costs and enhancing competitiveness.

5. Excellent alcohol resistance; excellent weather resistance, remains unchanged and not yellowed after 120 hours of UV aging test, easy to spray and oil.

6. Compatible with PU overcoat paint. Excellent interlayer adhesion; the PU varnish does not bite the bottom, turn black, or change color.

7. One-component application, featuring excellent scratch resistance, high hardness, quick drying, and good resistance to alcohol and ethanol (about 50 times resistance to 500克力 alcohol).

 Advantages: No need for anti-silver shedding additives, no silver powder shedding or paint chipping, solves issues such as poor adhesion and delamination between the electroplated silver primer and the topcoat PU glossy layer, and completely resolves paint chipping problems on transparent red or yellow coatings over electroplated silver undercoats.

Application Range: Aluminum silver powder added to over 10% point maintains no powder loss, suitable for assembly lines and spraying, with improved coverage and quicker coloring.

2618 is primarily used for producing ABS plastic electroplated silver oil, electroplated silver paint, furniture paint, and toy paint with electroplated silver effect.

2618 adheres well to soft PVC substrates, boasts excellent flexibility, tensile strength, adhesion, and resistance to ultraviolet light.

Instructions for Use:

Add an appropriate amount of electroplating silver paste to the 2618 non-silver electroplating silver resin, mix thoroughly, and it's ready to use. (Recommended dilution ratio 1:3 or higher)

Reference Formula: (Thinner-based Oil Water Formula)

2618 Electroplating Silver Oil Resin  75.5-79.5%   Butyl Acetate 72%   Ethyl Acetate 20%   Antistatic Water 8%

985 Simulated Electroplate Silver Paste 8-10%

n-Butyl acetate                 8-10%

Leveling Agent         0.5%

Produce according to this formula: It is recommended to dilute with water at a ratio of 1:2.5 or 1:3 before spraying.

Packaging: Net Weight 50kg/200kg Drum Packaging

Store in a cool, dry place, sealed, for up to 12 months without affecting quality.